1. SIVI LJEV
|
EN 1561 |
DIN 1691 |
JUS C.J2.020 |
Redni broj |
Skraćena oznaka |
Broj |
Skraćena oznaka |
Broj |
Stara oznaka |
1. |
EN-GJL-150 |
EN-JL 1020 |
GG-15 |
0.6015 |
SL 15 |
2. |
EN-GJL-200 |
EN-JL 1030 |
GG-20 |
0.6020 |
SL 20 |
3. |
EN-GJL-250 |
EN-JL 1040 |
GG-25 |
0.6025 |
SL 25 |
4. |
EN-GJL-300 |
EN-JL 1050 |
GG-30 |
0.6030 |
SL 30 |
2. NODURALNI LJEV
|
EN 1563 |
DIN 1693 |
JUS C.J2.022 |
Redni broj |
Skraćena oznaka |
Broj |
Skraćena oznaka |
Broj |
Stara oznaka |
1. |
EN-GJS-40-18-LT |
EN-JS1025 |
GGG-40.3 |
0.7043 |
NL 40.3* |
2. |
EN-GJS-40-15 |
EN-JS1030 |
GGG-40 |
0.7040 |
NL 40 |
3. |
EN-GJS-500-7 |
EN-JS1050 |
GGG-50 |
0.7050 |
NL 50 |
4. |
EN-GJS-600-3 |
EN-JS1060 |
GGG-60 |
0.7060 |
NL 60 |
5. |
EN-GJS-700-2 |
EN-JS1070 |
GGG-70 |
0.7070 |
NL 70 |
3. VERMIKULARNI LJEV
|
KEMIJSKI SASTAV, [%] |
Omjer
CG/SG
[%] |
Red. broj |
Oznake prema EN |
C |
Si |
S |
P |
Mn |
Mg,Ti |
Ostalo |
1. |
|
3.2
3.7 |
1.9
2.7 |
0.005
0.015 |
0.030
MAX |
0.20
MAX |
Ovisno o postupku |
Kao kod NL |
60/40 |
4. TVRDI LJEV
|
KEMIJSKI SASTAV, [%] |
Tvrdoća nakon toplinske obrade |
Red. broj |
Oznake prema DIN 1695 |
C |
Si |
Mn |
Cr |
Ni |
Mo |
Mo |
1. |
G-X 295 Cr26 |
2.7
3.0 |
<1 |
<1 |
26
28 |
|
<0.5 |
>=60 |
2. |
G-X 300 CrMoNi1521 |
2.3
3.6 |
0.2
0.8 |
0.5
1.0 |
14
17 |
<1.2 |
1.8
1.2 |
>=60 |
3. |
G-X 300 CrMo 153 |
3.2
3.6 |
0.3
0.8 |
0.4
0.9 |
14
16 |
|
2.5
3.0 |
>=60 |
5. ČELIČNI LJEV
|
KEMIJSKI SASTAV, [%] |
Red. broj |
Oznake prema EN |
Stara oznaka po JUS |
C |
S |
Si |
Cr |
Mn |
Mo |
P |
1. |
GS-42CrMo4 |
ČL 4732 |
0.38
0.45 |
0.015
MAX |
0.30
0.55 |
0.80
1.20 |
0.50
0.80 |
0.20
0.30 |
0.020
MAX |
|
|
Mehaničke osobine sivog ljeva
Oznaka ljeva |
Debljina stjenke |
Vlačna čvrstoća zahtijevana |
Vlačna čvrstoća |
Preko |
Do |
Odlivena proba |
Prilivena proba |
Očekivana vrijednost |
Skraćena oznaka |
Broj |
mm |
mm |
N/mm2 (min) |
N/mm2 (min) |
N/mm2 (min) |
EN 1561 |
EN 1561 |
- |
- |
- |
- |
- |
EN-GJL-150 |
EN-JL1020 |
2.5 |
5 |
150-250 |
- |
180 |
5 |
10 |
- |
155 |
10 |
20 |
- |
130 |
20 |
40 |
120 |
110 |
40 |
80 |
110 |
95 |
80 |
150 |
100 |
80 |
150 |
300 |
90 |
- |
EN-GJL-200 |
EN-JL1030 |
2.5 |
5 |
250-300 |
- |
230 |
5 |
10 |
- |
205 |
10 |
20 |
- |
180 |
20 |
40 |
170 |
155 |
40 |
80 |
150 |
130 |
80 |
150 |
140 |
115 |
150 |
300 |
130 |
- |
EN-GJL-250 |
EN-JL1040 |
5 |
10 |
300-350 |
- |
250 |
10 |
20 |
- |
225 |
20 |
40 |
210 |
195 |
40 |
80 |
190 |
170 |
80 |
150 |
170 |
155 |
150 |
300 |
160 |
- |
EN-GJL-300 |
EN-JL1050 |
10 |
20 |
350-400 |
- |
270 |
20 |
40 |
250 |
240 |
40 |
80 |
220 |
210 |
80 |
150 |
210 |
195 |
150 |
300 |
190 |
- |
Usporedne vrijednosti mehaničkih osobina sivog ljeva (SL), vermikularnog ljeva (CGI) i nodularnog ljeva (NL)
|
|
Tvrdoća |
Zatezna čvrstoća |
Granica rastezanja |
Izduženje |
Toplinska vodljivost |
Vrsta ljeva |
Osnova |
HB |
MPa |
MPa |
% |
W / Mk |
SL |
Perltna |
175-230 |
230-300 |
115-210 |
0-1 |
44-52 |
|
Ferlitna |
130-190 |
330-410 |
240-305 |
5-10 |
40-50 |
CGI |
Perltna |
215-250 |
400-580 |
345-415 |
2-5 |
31-42 |
|
Ferlitna |
140-200 |
400-600 |
285-315 |
15-25 |
32-38 |
NL |
Perltna |
240-300 |
600-700 |
375-482 |
3-10 |
25-32 |
Mehaničke osobine nodularnog ljeva od odlivenih proba
|
|
Vlačna čvrstoća |
0,2% granica istezanja |
Istezanje |
Oznaka materijala |
Rm |
RP 0.2 |
A |
Skraćena oznaka |
Broj |
N /mm2 (min) |
N /mm2 (min) |
% (min) |
EN-GJS-400-18-LT |
EN-JS 1025 |
400 |
240 |
18 |
EN-GJS-400-15 |
EN-JS 1030 |
400 |
250 |
15 |
EN-GJS-500-7 |
EN-JS 1050 |
500 |
320 |
7 |
EN-GJS-600-3 |
EN-JS 1060 |
600 |
370 |
3 |
EN-GJS-700-2 |
EN-JS 1070 |
700 |
420 |
2 |
|